Glastherm® HT 300
GFK-EP
Glastherm® HT 300 is designed for very high continuous operation temperatures over a long period. Its outstanding features include a long service life, very low weight loss and high dimensional stability. Glastherm® HT 300 also boasts excellent strength properties in high temperatures. The material structure is maintained over a very long period. Glastherm® HT 300 is free of asbestos and can be easily cut and adapted with standard metal tools.
- Maximum continuous operation temperature: 300 °C (572 °F)
- Very high compressive strength: 280 MPa (at 200 °C)
- Good thermal insulation
板
サイズ一覧
| 製品コード | 製品名 | 形状 | 形状 | 色 | 製品サイズ | 長さ | 幅 | 厚み | 高さ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 在庫あり(MOQなし) | 459580 | Glastherm® HT 300 white pressed | 板 | 板 | cream, similar RAL 9001 | 2.150 x 1.130 x 27 (+/-1,5) mm | 2,150 mm | 1,130 mm | 27 mm | ||
| 在庫あり(MOQなし) | 409321 | Glastherm® HT 300 pressed | 板 | 板 | 2.150 x 1.130 x 23 (+/-2) mm | 2,150 mm | 1,130 mm | 23 mm | |||
| 在庫あり(MOQなし) | 409323 | Glastherm® HT 300 pressed | 板 | 板 | 2.150 x 1.130 x 18 (+/-2) mm | 2,150 mm | 1,130 mm | 18 mm | |||
| 在庫あり(MOQなし) | 413353 | Glastherm® HT 300 pressed | 板 | 板 | 2.150 x 1.130 x 22 (+/-1) mm | 2,150 mm | 1,130 mm | 22 mm | |||
| 在庫なし(MOQあり) | 458207 | Glastherm® HT 300 pressed | 板 | 板 | 2.150 x 1.130 x 12 (+/-0,94) mm | 2,150 mm | 1,130 mm | 12 mm | |||
| 在庫なし(MOQあり) | 458499 | Glastherm® HT 300 pressed | 板 | 板 | 2.150 x 1.130 x 17 (+/-1,02) mm | 2,150 mm | 1,130 mm | 17 mm | |||
| 在庫あり(MOQなし) | 464106 | Glastherm® HT 300 pressed | 板 | 板 | 2.150 x 1.130 x 43 (+/-2,1) mm | 2,150 mm | 1,130 mm | 43 mm | |||
| 在庫あり(MOQなし) | 464459 | Glastherm® HT 300 pressed | 板 | 板 | 2.150 x 1.130 x 6 (+/-0,6) mm | 2,150 mm | 1,130 mm | 6 mm |
技術仕様書 Glastherm® HT 300
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | ISO 1183 | g / cm3 | 1,9 |
| 曲げ強度 ┴ | ISO 178 | MPa | 120 |
| たわみ荷重弾性係数┴ | ISO 178 | MPa | 15000 |
| 圧縮強度1)┴ | ISO 604 | MPa | 330 |
| 圧縮強度1)┴ +200°C | ISO 604 | MPa | 280 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 熱伝導率2)┴ | W / (m * K) | ≈ 0,28 | |
| 線膨張係数 II | TMA (Mettler) | 10-6 x K-1 | ≈ 10 - 15 |
| 最高連続使用温度 | °C | 300 |