Sustarin® C GF 25 black
POM-C
The glass fibre-reinforced polyacetal
Compared to unfilled Sustarin® C, Sustarin® C GF 25 is characterised above all by its increased rigidity and higher dimensional stability. The glass fibre-reinforced material is therefore particularly suitable for applications that require low deformation of the material under mechanical load, even at elevated temperatures of up to 100°C and long load durations. Sliding applications are not recommended, as the glass fibres are abrasive to most mating materials, including steel.
black
丸棒
特性
- 高剛性
- 優れた寸法安定性
- 低吸湿性
- 高いクリープ耐性
- 高い弾性率
- 高い硬度
用途例
サイズ一覧
技術仕様書 Sustarin® C GF 25 black
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | DIN EN ISO 1183-1 | g / cm3 | 1,58 |
| 吸水率 | DIN EN ISO 62 | % | 0,2 |
| 燃焼性 (厚み 3 mm / 6 mm) | UL 94 | HB / HB |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 引張降伏応力 | DIN EN ISO 527 | MPa | 65 |
| 引張破壊呼び歪 | DIN EN ISO 527 | % | 3 |
| 引張弾性率 | DIN EN ISO 527 | MPa | 4500 |
| ノッチ付き衝撃耐性 | DIN EN ISO 179 | kJ / m2 | 4 |
| ショア硬度 | DIN EN ISO 868 | scale D | 85 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 融点 | ISO 11357-3 | °C | 165 |
| 線膨張係数 | DIN 53752 | 10-6 / K | 30 |
| 使用温度（長期） | 平均値 | °C | -20 … 100 |
| 使用温度（短期、最大） | 平均値 | °C | 140 |
| 荷重たわみ温度 | DIN EN ISO 75, Verf. A, HDT | °C | 160 |