Polystone® P HG EHS white
PP
High-performance polypropylene especially for the Healthcare industry
In addition to its good hot steam sterilizability, this special material has good machinability and excellent chemical resistance. Polystone® P HG EHS is an isotactic, highly heat-stabilized polypropylene that is available as a homopolymer. This unique property profile makes it perfect for components for respiratory equipment or for applications in the pharmaceutical industry, either as a distribution unit, components for drug production or in chromatography.
white, similar RAL 9010
丸棒
We are a system supplier and partner from the idea to the OEM's end product - as a cooperative value contribution. We are able to support the healthcare industry at the highest level.
Industry Manager Healthcare - Mail: AReuner@roechling.com
サイズ一覧
| 製品コード | 製品名 | 形状 | 形状 | 色 | 製品サイズ | 長さ | 幅 | 厚み | 高さ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 在庫なし(MOQあり) | 870705 | Polystone® P HG EHS white extruded | 丸棒 | 丸棒 | white, similar RAL 9010 | Ø 80 x 3000 mm | 3,000 mm | 80 mm | |||
| 在庫なし(MOQあり) | 870706 | Polystone® P HG EHS white extruded | 丸棒 | 丸棒 | white, similar RAL 9010 | Ø 80 x 1000 mm | 1,000 mm | 80 mm |
技術仕様書 Polystone® P HG EHS white extruded
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | DIN EN ISO 1183-1 | g / cm3 | 0,92 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 引張破壊呼び歪 | DIN EN ISO 527 | % | 40 |
| 引張弾性率 | DIN EN ISO 527 | MPa | 1500 |
| 引張強度 | DIN EN ISO 527 | MPa | 35 |
| ノッチ付き衝撃耐性 | DIN EN ISO 179 | kJ / m2 | 4,5 |
| ボールインデンテーション硬度 | DIN EN ISO 2039-1 | MPa | 80 |
| 硬度 | DIN EN ISO 868 | Shore D | 75 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 融点 | ISO 11357-3 | °C | 163 |
技術仕様書 Polystone® P HG EHS white pressed
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | DIN EN ISO 1183-1 | g / cm3 | >0,91 |
| 吸水率 | DIN EN ISO 62 | % | 0,10 |
| 燃焼性 (厚み 3 mm / 6 mm) | UL 94 | HB |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 引張降伏応力 | DIN EN ISO 527 | MPa | >30 |
| 引張弾性率 | DIN EN ISO 527 | MPa | >1800 |
| ノッチ付き衝撃耐性 | DIN EN ISO 179 | kJ / m2 | >6 |
| ショア硬度 | DIN EN ISO 868 | scale D | >70 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 融点 | ISO 11357-3 | °C | 162 ... 167 |
| 熱伝導率 | DIN 52612-1 | W / (m * K) | 0,20 |
| 熱容量 | DIN 52612 | kJ / (kg * K) | 1,70 |
| 線膨張係数 | DIN 53752 | 10-6 / K | 120 ... 190 |
| 荷重たわみ温度 | DIN EN ISO 75, Verf. A, HDT | °C | 90 |
| Autoclaving temperature resistance | 平均値 | °C | 0 ... 135 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 体積固有抵抗 | DIN EN 62631-3-1 | Ω * cm | >1014 |
| 表面固有抵抗 | DIN EN 62631-3-2 | Ω | >1014 |
| 絶縁破壊電圧 | IEC 60243 | kV / mm | >40 |