Polystone® G HG white
PE — PE-HD - PE 300
High-performance polyethylene especially for the Healthcare industry
Due to its excellent chemical resistance, hygienic surface and high stability, it offers a wide range of possible applications in the healthcare sector – especially to produce complex components. From pharmaceutical production and analytical processes to innovative transport solutions - this material can make a significant contribution to optimising processes, cost-effectiveness and increasing product safety.
white, similar RAL 9010
板
We are a system supplier and partner from the idea to the OEM's end product - as a cooperative value contribution. We are able to support the healthcare industry at the highest level.
Industry Manager Healthcare - Mail: AReuner@roechling.com
サイズ一覧
| 製品コード | 製品名 | 形状 | 形状 | 色 | 製品サイズ | 長さ | 幅 | 厚み | 高さ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 在庫なし(MOQあり) | 504509 | Polystone® G HG white extruded | 板 | 板 | white, similar RAL 9010 | 15 x 1500 x 3000 mm | 3,000 mm | 1,500 mm | 15 mm | ||
| 在庫なし(MOQあり) | 504510 | Polystone® G HG white extruded | 板 | 板 | white, similar RAL 9010 | 20 x 1500 x 3000 mm | 3,000 mm | 1,500 mm | 20 mm | ||
| 在庫なし(MOQあり) | 504513 | Polystone® G HG white extruded | 板 | 板 | white, similar RAL 9010 | 10 x 1500 x 3000 mm | 3,000 mm | 1,500 mm | 10 mm | ||
| 在庫なし(MOQあり) | 504514 | Polystone® G HG white extruded | 板 | 板 | white, similar RAL 9010 | 15 x 2000 x 3000 mm | 3,000 mm | 2,000 mm | 15 mm | ||
| 在庫なし(MOQあり) | 505286 | Polystone® G HG white extruded | 板 | 板 | white, similar RAL 9010 | 30 x 1500 x 3000 mm | 3,000 mm | 1,500 mm | 30 mm | ||
| 在庫なし(MOQあり) | 505287 | Polystone® G HG white extruded | 板 | 板 | white, similar RAL 9010 | 6 x 1500 x 3000 mm | 3,000 mm | 1,500 mm | 6 mm | ||
| 在庫なし(MOQあり) | 507378 | Polystone® G HG white pressed | 板 | 板 | white, similar RAL 9010 | 60 x 1000 x 2000 mm | 2,000 mm | 1,000 mm | 60 mm |
技術仕様書 Polystone® G HG white extruded
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | DIN EN ISO 1183-1 | g / cm3 | >0,95 |
| 吸水率 | DIN EN ISO 62 | % | 0,01 |
| 燃焼性 (厚み 3 mm / 6 mm) | UL 94 | HB |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 引張降伏応力 | DIN EN ISO 527 | MPa | >22 |
| 引張破壊呼び歪 | DIN EN ISO 527 | % | >50 |
| 引張弾性率 | DIN EN ISO 527 | MPa | >1000 |
| ノッチ付き衝撃耐性 | DIN EN ISO 179 | kJ / m2 | >13 |
| ショア硬度 | DIN EN ISO 868 | scale D | >61 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 融点 | ISO 11357-3 | °C | 130 ... 135 |
| 熱伝導率 | DIN 52612-1 | W / (m * K) | 0,40 |
| 熱伝導率 | DIN EN ISO 8302 | W / (m * K) | 1,90 |
| 線膨張係数 | DIN 53752 | 10-6 / K | 150 ... 230 |
| 使用温度（長期） | 平均値 | °C | -50 … 80 |
| 使用温度（短期、最大） | 平均値 | °C | 100 |
| ビカットB軟化温度 | DIN EN ISO 306, Vicat B | °C | 67 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 誘電率 | IEC 60250 | 2,4 | |
| 誘電正接 (106 Hz) | IEC 60250 | 0,0004 | |
| 体積固有抵抗 | DIN EN 62631-3-1 | Ω * cm | >1014 |
| 表面固有抵抗 | DIN EN 62631-3-2 | Ω | >1014 |
| 比較トラッキング指数 | IEC 60112 | 600 | |
| 絶縁破壊電圧 | IEC 60243 | kV / mm | >40 |
技術仕様書 Polystone® G HG white pressed
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | DIN EN ISO 1183-1 | g / cm3 | >0,95 |
| 吸水率 | DIN EN ISO 62 | % | 0,01 |
| 燃焼性 (厚み 3 mm / 6 mm) | UL 94 | HB |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 引張降伏応力 | DIN EN ISO 527 | MPa | >22 |
| 引張破壊呼び歪 | DIN EN ISO 527 | % | >50 |
| 引張弾性率 | DIN EN ISO 527 | MPa | >1000 |
| ノッチ付き衝撃耐性 | DIN EN ISO 179 | kJ / m2 | >13 |
| ショア硬度 | DIN EN ISO 868 | scale D | >61 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 融点 | ISO 11357-3 | °C | 130 ... 135 |
| 熱伝導率 | DIN 52612-1 | W / (m * K) | 0,40 |
| 熱伝導率 | DIN EN ISO 8302 | W / (m * K) | 1,90 |
| 線膨張係数 | DIN 53752 | 10-6 / K | 150 ... 230 |
| 使用温度（長期） | 平均値 | °C | -50 … 80 |
| 使用温度（短期、最大） | 平均値 | °C | 100 |
| ビカットB軟化温度 | DIN EN ISO 306, Vicat B | °C | 67 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 誘電率 | IEC 60250 | 2,4 | |
| 誘電正接 (106 Hz) | IEC 60250 | 0,0004 | |
| 体積固有抵抗 | DIN EN 62631-3-1 | Ω * cm | >1014 |
| 表面固有抵抗 | DIN EN 62631-3-2 | Ω | >1014 |
| 比較トラッキング指数 | IEC 60112 | 600 | |
| 絶縁破壊電圧 | IEC 60243 | kV / mm | >40 |