SustaPEI GF 30 natural
PEI
The Reinforced Amorphous High Performance Polymer
The addition of 30 % glass fibre by weight increases the mechanical strength and rigidity compared to unfilled PEI across the entire application temperature range to an even higher level. At the same time, the thermal expansion coefficient is lower. SustaPEI GF30 is therefore particularly suitable for components that are subject to high mechanical loads and require high dimensional stability. Application temperatures of up to ap 170°C continuously and 190°C for short periods are possible.
natural
丸棒
サイズ一覧
| 製品コード | 製品名 | 形状 | 形状 | 色 | 製品サイズ | 長さ | 幅 | 厚み | 高さ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 在庫なし(MOQあり) | 696851 | SustaPEI GF 30 natural extruded | 丸棒 | 丸棒 | natural | Ø 80 x 3000 mm | 3,000 mm | 80 mm | |||
| 在庫なし(MOQあり) | 697173 | SustaPEI GF 30 natural extruded | 丸棒 | 丸棒 | natural | Ø 80 x 1000 mm | 1,000 mm | 80 mm | |||
| 在庫なし(MOQあり) | 700289 | SustaPEI GF 30 natural extruded | 丸棒 | 丸棒 | natural | Ø 110 x 1000 mm | 1,000 mm | 110 mm |
技術仕様書 SustaPEI GF 30 natural
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | DIN EN ISO 1183-1 | g / cm3 | 1,51 |
| 吸水率 | DIN EN ISO 62 | % | 0,4 |
| 燃焼性 (厚み 3 mm / 6 mm) | UL 94 | V0 / V0 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 引張降伏応力 | DIN EN ISO 527 | MPa | 120 |
| 引張破壊呼び歪 | DIN EN ISO 527 | % | 4 |
| 引張弾性率 | DIN EN ISO 527 | MPa | 5000 |
| ショア硬度 | DIN EN ISO 868 | scale D | 92 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 融点 | ISO 11357-3 | °C | - |
| ガラス転移温度 | ISO 11357-3 | °C | 217 |
| 使用温度（長期） | 平均値 | °C | -30 … 170 |
| 使用温度（短期、最大） | 平均値 | °C | 210 |
| 荷重たわみ温度 | DIN EN ISO 75, Verf. A, HDT | °C | 210 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 誘電率 | IEC 60250 | 3,3 | |
| 誘電正接 (50 Hz) | IEC 60250 | 0,0016 | |
| 体積固有抵抗 | DIN EN 62631-3-1 | Ω * cm | 1015 |
| 表面固有抵抗 | DIN EN 62631-3-2 | Ω | 1015 |
| 比較トラッキング指数 | IEC 60112 | 150 | |
| 絶縁破壊電圧 | IEC 60243 | kV / mm | 35 |