SustaPEEK GF 30 black
PEEK
The Reinforced Premium Material
The addition of 30 % glass fibre increases the mechanical strength and stiffness compared to unfilled PEEK across the entire application temperature range. At the same time, the coefficient of thermal expansion is lower. SustaPEEK GF30 is therefore particularly suitable for mechanically highly stressed, very dimensionally stable components, especially at temperatures above the glass transition temperature (150°C).
black
丸棒
サイズ一覧
| 製品コード | 製品名 | 形状 | 形状 | 色 | 製品サイズ | 長さ | 幅 | 厚み | 高さ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| 在庫なし(MOQあり) | 931974 | SustaPEEK GF 30 black extruded | 丸棒 | 丸棒 | black | Ø 75 x 3000 mm | 3,000 mm | 75 mm | |||
| 在庫なし(MOQあり) | 931975 | SustaPEEK GF 30 black extruded | 丸棒 | 丸棒 | black | Ø 75 x 1000 mm | 1,000 mm | 75 mm |
技術仕様書 SustaPEEK GF 30 black
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | DIN EN ISO 1183-1 | g / cm3 | 1,49 |
| 吸水率 | DIN EN ISO 62 | % | 0,1 |
| 燃焼性 (厚み 3 mm / 6 mm) | UL 94 | V0 / V0 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 引張降伏応力 | DIN EN ISO 527 | MPa | 80 |
| 引張破壊呼び歪 | DIN EN ISO 527 | % | 5 |
| 引張弾性率 | DIN EN ISO 527 | MPa | 6000 |
| ノッチ付き衝撃耐性 | DIN EN ISO 179 | kJ / m2 | 3,0 |
| ショア硬度 | DIN EN ISO 868 | scale D | 89 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 融点 | ISO 11357-3 | °C | 343 |
| 熱伝導率 | DIN 52612-1 | W / (m * K) | 0,43 |
| 線膨張係数 | DIN 53752 | 10-6 / K | 30 |
| 使用温度（長期） | 平均値 | °C | -20 … 250 |
| 使用温度（短期、最大） | 平均値 | °C | 310 |
| 荷重たわみ温度 | DIN EN ISO 75, Verf. A, HDT | °C | 315 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 誘電率 | IEC 60250 | 3,2 | |
| 誘電正接 (50 Hz) | IEC 60250 | 0,001 | |
| 体積固有抵抗 | DIN EN 62631-3-1 | Ω * cm | 1014 |
| 表面固有抵抗 | DIN EN 62631-3-2 | Ω | 1013 |
| 比較トラッキング指数 | IEC 60112 | 175 | |
| 絶縁破壊電圧 | IEC 60243 | kV / mm | 20 |