Glastherm® HT 200 (SMC)
GFK-UP
Glastherm® HT 200 is a heat insulation system with a high level of stability which is suitable for processes with a working temperature of up to 200 °C (392 °F). Glastherm® HT 200 was developed specially for plastic and zinc die-casting moulds. It has good thermal insulation, enabling rapid die heating-up processes and therefore rapid start-up of the machines. Glastherm® HT 200 is free of asbestos and can be easily cut and adapted with standard metal tools.
- Maximum continuous operation temperature: 200 °C (392 °F)
- High compressive strength: 230 MPa (at 200 °C)
- Good thermal insulation
技術仕様書 Glastherm® HT 200 (SMC)
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 密度 | ISO 1183 | g / cm3 | 1,8 |
| 曲げ強度 ┴ | ISO 178 | MPa | 200 |
| たわみ荷重弾性係数┴ | ISO 178 | MPa | 12000 |
| 圧縮強度1)┴ | ISO 604 | MPa | 320 |
| 圧縮強度1)┴ +200°C | ISO 604 | MPa | 160 |
| 引張強度II | ISO 527 | MPa | 120 |
| 衝撃強度(シャルピー衝撃試験)┴ | ISO 179 | kJ / m2 | 60 |
| Splitting force II | DIN 53463 | N | 2200 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 熱伝導率2)┴ | W / (m * K) | ≈ 0,3 | |
| 線膨張係数 II | TMA (Mettler) | 10-6 x K-1 | ≈ 20 |
| 最高連続使用温度 | °C | 200 |
| 試験法 | 単位 | 数値 | |
|---|---|---|---|
| 吸水率 ( (method 1) | ISO 62 | % | 0,1 |