Glastherm® HT 200

GFK-UP

Glastherm^® HT 200 is a heat insulation system with a high level of stability which is suitable for processes with a working temperature of up to 200 °C (392 °F). Glastherm^® HT 200 was developed specially for plastic and zinc die-casting moulds. It has good thermal insulation, enabling rapid die heating-up processes and therefore rapid start-up of the machines. Glastherm^® HT 200 is free of asbestos and can be easily cut and adapted with standard metal tools.

Maximum continuous operation temperature: 200 °C (392 °F)
High compressive strength: 230 MPa (at 200 °C)
Good thermal insulation

板機械部品

特性

断熱用途に開発された繊維強化複合材料

用途例

サイズ一覧

	製品コード	製品名	形状	形状	製品サイズ	長さ	幅	厚み
在庫なし(MOQあり)	428269	Glastherm® HT 200 pressed	板	板	2.445 x 1.255 x 22 mm	2,445 mm	1,255 mm	22 mm
在庫なし(MOQあり)	443422	Glastherm® HT 200 pressed	板	板	2.445 x 1.255 x 27 mm	2,445 mm	1,255 mm	27 mm
在庫なし(MOQあり)	447666	Glastherm® HT 200 pressed	板	板	2.445 x 1.255 x 12 (+/-0,1) mm	2,445 mm	1,255 mm	12 mm
在庫なし(MOQあり)	505348	Glastherm® HT 200 pressed	機械部品	機械部品	2.046 x 327,5 x 20 (+/-0,1) mm	2,046 mm	327.5 mm	20 mm
在庫なし(MOQあり)	505352	Glastherm® HT 200 pressed	機械部品	機械部品	1.532,5 x 216 x 20 (+/-0,1) mm	1,532.5 mm	216 mm	20 mm
在庫なし(MOQあり)	505354	Glastherm® HT 200 pressed	機械部品	機械部品	1.035 x 216 x 20 (+/-0,1) mm	1,035 mm	216 mm	20 mm

技術仕様書 Glastherm® HT 200

機械的物性

	試験法	単位	数値
密度	ISO 1183	g / cm³	1,9
曲げ強度 ┴	ISO 178	MPa	200
たわみ荷重弾性係数┴	ISO 178	MPa	12000
圧縮強度¹⁾┴	ISO 604	MPa	320
圧縮強度¹⁾┴ +200°C	ISO 604	MPa	230
引張強度II	ISO 527	MPa	120
衝撃強度(シャルピー衝撃試験)┴	ISO 179	kJ / m²	100
Splitting force II	DIN 53463	N	2200