Polystone® PPs EL black
PP-H
black, similar RAL 9005
sheetwelding rod
Characteristics
- Flame retardant
- Antistatic
- Electrically conductive
Variants
Technical Specifications Polystone® PPs EL black extruded
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Hustota | DIN EN ISO 1183-1 | g / cm3 | >1,17 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V0 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >20 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1300 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >4 |
| Shore hardness | DIN EN ISO 868 | scale D | >65 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | >145 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,22 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 120 ... 190 |
| Service temperature, long term | Average | °C | 0 … 100 |
| Service temperature, short term (max.) | Average | °C | 130 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 81 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 105 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 105 |
Technical Specifications Polystone® PPs EL black pressed
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Hustota | DIN EN ISO 1183-1 | g / cm3 | >1,17 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V0 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >20 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1300 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >4 |
| Shore hardness | DIN EN ISO 868 | scale D | >65 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | >145 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,22 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 120 ... 190 |
| Service temperature, long term | Average | °C | 0 … 100 |
| Service temperature, short term (max.) | Average | °C | 130 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 81 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 105 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 105 |