Sustamid® 6G MO černý
PA — PA 6 G
MoS₂-reinforced polyamide - optimized for sliding and abrasion loads
Sustamid® 6G M anthracite is a shape-polymerized polyamide 6 modified with molybdenum disulphide (MoS₂). Compared to the unmodified grade Sustamid® 6G, it has a higher MoS₂ content, which leads to an increased degree of crystallization and a fine, homogeneous microstructure. This results in greater hardness and a slightly higher modulus of elasticity. The material also offers very good sliding and abrasion properties.
blackblack, similar RAL 9005
sheetrodbloctubular bar
Characteristics
- High rigidity
- High toughness even at high temperatures
- UV-resistant
- High absorption of moisture of up to 3 % in standard atmosphere
Variants
Technical Specifications Sustamid® 6G MO black
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Hustota | DIN EN ISO 1183-1 | g / cm3 | 1,15 |
| Absorpce vody | DIN EN ISO 62 | % | 2,5 |
| Hořlavost (tloušťka 3 mm / 6 mm) | UL 94 | HB / HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Mez kluzu | DIN EN ISO 527 | MPa | 82 |
| Prodloužení při přetržení | DIN EN ISO 527 | % | 35 |
| Modul pružnosti v tahu | DIN EN ISO 527 | MPa | 3500 |
| Vrubová houževnatost | DIN EN ISO 179 | kJ / m2 | 2,5 |
| Tvrdost Shore | DIN EN ISO 868 | scale D | 83 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Teplota tání | ISO 11357-3 | °C | 216 |
| Tepelná vodivost | DIN 52612-1 | W / (m * K) | 0,25 |
| Tepelná kapacita | DIN 52612 | kJ / (kg * K) | 1,70 |
| Koeficient lineární teplotní roztažnosti | DIN 53752 | 10-6 / K | 80 |
| Provozní teplota dlouhodobá | Průměr | °C | -40 … 110 |
| Provozní teplota krátkodobá (max.) | Průměr | °C | 170 |
| Teplota tepelné deformace | DIN EN ISO 75, Verf. A, HDT | °C | 95 |