Sustamid® 6G LL přírodní
PA — PA 6 G
PA 6G with optimized combination of hardness and impact strength
Sustamid® 6 GLL is a shape-polymerized polyamide 6 modified with an impact-resistant monomer. The material offers increased toughness and is particularly suitable for components that are exposed to shock and impact loads.
natural
blocrodtubular bar
Characteristics
- Good sliding properties
- Good wear properties
- Good machinability
- Good impact strength
Variants
Technical Specifications Sustamid® 6G LL natural
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Hustota | DIN EN ISO 1183-1 | g / cm3 | 1,13 |
| Absorpce vody | DIN EN ISO 62 | % | 2,3 |
| Hořlavost (tloušťka 3 mm / 6 mm) | UL 94 | HB / V2 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Mez kluzu | DIN EN ISO 527 | MPa | 64 |
| Prodloužení při přetržení | DIN EN ISO 527 | % | 50 |
| Modul pružnosti v tahu | DIN EN ISO 527 | MPa | 2700 |
| Vrubová houževnatost | DIN EN ISO 179 | kJ / m2 | 5 |
| Tvrdost Shore | DIN EN ISO 868 | scale D | 80 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Teplota tání | ISO 11357-3 | °C | 209 |
| Tepelná vodivost | DIN 52612-1 | W / (m * K) | 0,27 |
| Tepelná kapacita | DIN 52612 | kJ / (kg * K) | 1,70 |
| Koeficient lineární teplotní roztažnosti | DIN 53752 | 10-6 / K | 80 |
| Provozní teplota dlouhodobá | Průměr | °C | -40 … 110 |
| Provozní teplota krátkodobá (max.) | Průměr | °C | 170 |
| Teplota tepelné deformace | DIN EN ISO 75, Verf. A, HDT | °C | 95 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Relativní permitivita | IEC 60250 | 3,7 | |
| Dielektrický disipační faktor (50 Hz) | IEC 60250 | 0,02 | |
| Objemový odpor | DIN EN 62631-3-1 | Ω * cm | 1015 |
| Povrchový odpor | DIN EN 62631-3-2 | Ω | 1013 |
| Srovnávací sledovací index | IEC 60112 | 600 | |
| Dielektrická pevnost | IEC 60243 | kV / mm | 20 |