Test Method | Unit | Guideline Value | |
---|---|---|---|
Density | DIN EN ISO 1183-1 | g / cm3 | 0,65 |
Water absorption | DIN EN ISO 62 | % | <0,1 |
Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Yield stress | DIN EN ISO 527 | MPa | >17 |
Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >950 |
Notched impact strength | DIN EN ISO 179 | kJ / m2 | >15 |
Shore hardness | DIN EN ISO 868 | scale D | >65 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Melting temperature | ISO 11357-3 | °C | 162 ... 167 |
Thermal conductivity | DIN 52612-1 | W / (m * K) | <0,15 |
Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 120 ... 190 |
Service temperature, long term | Average | °C | -10 ... 90 |
Service temperature, short term (max.) | Average | °C | 150 |
Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 80 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Dielectric constant | IEC 60250 | 2,3 | |
Volume resistivity | DIN EN 62631-3-1 | Ohm * cm | >1014 |
Surface resistivity | DIN EN 62631-3-2 | Ohm | >1014 |