| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 377606 | Foamlite® G 752 + UV-stabilized black extruded | 2.440 x 1.220 x 15 mm | 2.440 mm | 1.220 mm | 15 mm | |||||
| No stock item (MOQ) | 377607 | Foamlite® G 752 + UV-stabilized black extruded | 2.440 x 1.220 x 19 mm | 2.440 mm | 1.220 mm | 19 mm | |||||
| No stock item (MOQ) | 408554 | Foamlite® G 752 + UV-stabilized black extruded | 2.440 x 1.220 x 10 mm | 2.440 mm | 1.220 mm | 10 mm | |||||
| No stock item (MOQ) | 408555 | Foamlite® G 752 + UV-stabilized black extruded | 2.440 x 1.220 x 12 mm | 2.440 mm | 1.220 mm | 12 mm | |||||
| No stock item (MOQ) | 415450 | Foamlite® G 752 + UV-stabilized black extruded | 1.220 x 1.220 x 10 mm | 1.220 mm | 1.220 mm | 10 mm | |||||
| No stock item (MOQ) | 474081 | Foamlite® G 752 + UV-stabilized black extruded | 3.000 x 1.500 x 10 mm | 3.000 mm | 1.500 mm | 10 mm | |||||
| No stock item (MOQ) | 474082 | Foamlite® G 752 + UV-stabilized black extruded | 3.000 x 1.500 x 15 mm | 3.000 mm | 1.500 mm | 15 mm | |||||
| No stock item (MOQ) | 477988 | Foamlite® G 752 + UV-stabilized black extruded | 2.440 x 1.220 x 12,7 mm | 2.440 mm | 1.220 mm | 12,7 mm | |||||
| No stock item (MOQ) | 478423 | Foamlite® G 752 + UV-stabilized black extruded | 3.000 x 2.000 x 10 mm | 3.000 mm | 2.000 mm | 10 mm | |||||
| No stock item (MOQ) | 478424 | Foamlite® G 752 + UV-stabilized black extruded | 3.000 x 2.000 x 15 mm | 3.000 mm | 2.000 mm | 15 mm |
Technical Specifications Foamlite® G 752 + UV-stabilized black
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 0,75 |
| Water absorption | DIN EN ISO 62 | % | <0,1 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >15 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >600 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >6 |
| Shore hardness | DIN EN ISO 868 | scale D | >62 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 133 ... 135 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,30 - 0,40 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,90 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -30 … 80 |
| Service temperature, short term (max.) | Average | °C | 100 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 67 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,5 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,0004 | |
| Volume resistivity | DIN EN 62631-3-1 | Ohm * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ohm | >1014 |