Sustarin® C green

POM-C

turquoise green, similar RAL 6016yellow green, similar RAL 6018greentraffic green, similar RAL 6024
rodsheet
QR-Code

Characteristics

  • Chemical resistance
  • Low moisture absorption
  • High abrasion resistance
  • ideal combination of tensile strength, stiffness and impact strength
  • Low creep tendency
  • Good machinability
  • favourable electric and dielectric behaviour
  • Good dimensional stability
  • Good sliding properties

Industries

Application Examples

+

Componenti per ROV

I sottomarini a comando remoto (ROV) vengono progettati per l’utilizzo in acque sempre più profonde. Noi vi supportiamo nello sviluppo con la nostra ampia gamma di materiali leggeri e resistenti alla corrosione, come Polystone® P e Polystone® D, intrinsecamente galleggianti, pensati per la costruzione del telaio. Le scatole elettroniche in Sustarin® C, a loro volta, sono più leggere delle tradizionali scatole elettroniche in metallo e, al tempo stesso resistenti alla corrosione. Gli ugelli di comando in Sustamid® 6G, un materiale leggero, resistente alla corrosione e agli urti, sono robusti e longevi.

+

Spezzatrice arrotondatrice per panini

Nella produzione industriale di panini i materiali di Röchling contribuiscono all’efficienza del processo produttivo: il tamburo della camera in Sustarin® C ruota nel senso inverso al tamburo di arrotondamento in Sustamid® 6G, formando in questo modo le palline di pasta.

+

Connettori

Le attrezzature e gli impianti sottomarini sono sempre più esigenti. Pertanto, i connettori per l’elettronica e la comunicazione devono essere prodotti in materiali di altissima qualità. I nostri materiali SustaPEEK®, SustaPEI® e Sustarin® C si adattano perfettamente all’impiego in impianti a secco (Dry-Mate) e a umido (Wet-Mate), grazie all’ottima resistenza elettronica e all’urto, al basso assorbimento di umidità e alla stabilità dimensionale.

+

Albero di Natale sottomarino – tappi di chiusura

Prima e dopo l’installazione dell’albero di Natale sottomarino, la bocca del pozzo deve essere dotata di un tappo di chiusura. Il peso dei tappi di chiusura ha un ruolo importante poiché l’installazione viene eseguita utilizzando sottomarini a comando remoto (ROV). I nostri materiali plastici Sustarin® C, SustaPVDF® e SustaPEEK® hanno un peso molto ridotto rispetto ai materiali tradizionali come il metallo e, al tempo stesso, sono altamente resistenti alla corrosione e agli agenti antincrostazioni e hanno un buon isolamento termico.

+

Aste

Barre tonde in Sustarin® C.

+

Prodotti ESD e antistatici per la produzione di compresse

Problematica: Il cliente richiedeva materiali antistatici per i prodotti coinvolti nella produzione di farmaci in polvere Materiali utilizzati: Polystone® G EL utilizzato per porte per guanti, Polystone® M AST utilizzato per scivoli e tubi, Sustarin® C ESD utilizzato per i collettori, Fibracon® PTFE AS utilizzato per le guarnizioni e i collegamenti flessibili I materiali ESD e AS dissipano l'accumulo statico generato dal movimento delle polveri Ampia gamma di temperature e detergenti

Variants

Show product in Webshop
SKUNameTypeTypeColorMeasurementsLengthWidthThicknessHeight
No stock item (MOQ)		141459Sustarin® C green extruded rod rod turquoise green, similar RAL 6016Ø 40 x 3000 mm 3.000 mm 40 mm
No stock item (MOQ)		600870Sustarin® C green extruded rod rod yellow green, similar RAL 6018Ø 10 x 3000 mm 3.000 mm 10 mm
No stock item (MOQ)		600871Sustarin® C green extruded rod rod greenØ 10 x 3000 mm 3.000 mm 10 mm
No stock item (MOQ)		627313Sustarin® C green extruded sheet sheet turquoise green, similar RAL 601660 x 620 x 2000 mm 2.000 mm 620 mm 60 mm
No stock item (MOQ)		646004Sustarin® C green extruded sheet sheet turquoise green, similar RAL 601630 x 620 x 2000 mm 2.000 mm 620 mm 30 mm
No stock item (MOQ)		646676Sustarin® C green extruded sheet sheet turquoise green, similar RAL 601640 x 620 x 2000 mm 2.000 mm 620 mm 40 mm
No stock item (MOQ)		720945Sustarin® C green extruded rod rod turquoise green, similar RAL 6016Ø 75 x 3000 mm 3.000 mm 75 mm
No stock item (MOQ)		720974Sustarin® C green extruded rod rod turquoise green, similar RAL 6016Ø 75 x 1000 mm 1.000 mm 75 mm
No stock item (MOQ)		722641Sustarin® C green extruded sheet sheet turquoise green, similar RAL 601630 x 620 x 3000 mm 3.000 mm 620 mm 30 mm
No stock item (MOQ)		751111Sustarin® C green extruded sheet sheet turquoise green, similar RAL 601660 x 620 x 1000 mm 1.000 mm 620 mm 60 mm
No stock item (MOQ)		755978Sustarin® C green extruded rod rod turquoise green, similar RAL 6016Ø 80 x 3000 mm 3.000 mm 80 mm
No stock item (MOQ)		755980Sustarin® C green extruded rod rod turquoise green, similar RAL 6016Ø 80 x 1000 mm 1.000 mm 80 mm
No stock item (MOQ)		757163Sustarin® C green extruded rod rod turquoise green, similar RAL 6016Ø 25 x 3000 mm 3.000 mm 25 mm
No stock item (MOQ)		763582Sustarin® C green extruded sheet sheet traffic green, similar RAL 602425 x 620 x 3000 mm 3.000 mm 620 mm 25 mm
No stock item (MOQ)		803936Sustarin® C green extruded rod rod turquoise green, similar RAL 6016Ø 40 x 1000 mm 1.000 mm 40 mm
No stock item (MOQ)		934435Sustarin® C green extruded rod rod greenØ 30 x 3000 mm 3.000 mm 30 mm
No stock item (MOQ)		934681Sustarin® C green extruded rod rod greenØ 30 x 1000 mm 1.000 mm 30 mm
No stock item (MOQ)		934835Sustarin® C green extruded rod rod yellow green, similar RAL 6018Ø 160 x 1000 mm 1.000 mm 160 mm

Technical Specifications Sustarin® C green

Test MethodUnitGuideline Value
DensityDIN EN ISO 1183-1g / cm31,41
Water absorptionDIN EN ISO 62%0,2
Flammability (Thickness 3 mm / 6 mm)UL 94HB / HB
Test MethodUnitGuideline Value
Yield stressDIN EN ISO 527MPa67
Elongation at breakDIN EN ISO 527%30
Tensile modulus of elasticityDIN EN ISO 527MPa2800
Notched impact strengthDIN EN ISO 179kJ / m26
Shore hardnessDIN EN ISO 868scale D81
Test MethodUnitGuideline Value
Melting temperatureISO 11357-3°C165
Thermal conductivityDIN 52612-1W / (m * K)0,31
Thermal capacityDIN 52612kJ / (kg * K)1,50
Coefficient of linear thermal expansionDIN 5375210-6 / K110
Service temperature, long termAverage°C-50 … 100
Service temperature, short term (max.)Average°C140
Heat deflection temperatureDIN EN ISO 75, Verf. A, HDT°C110
Test MethodUnitGuideline Value
Dielectric constantIEC 602503,8
Dielectric dissipation factor (50 Hz)IEC 602500,002
Volume resistivityDIN EN 62631-3-1Ohm * cm1013
Surface resistivityDIN EN 62631-3-2Ohm1013
Comparative tracking indexIEC 60112600
Dielectric strengthIEC 60243kV / mm40

Contact

You have the option of attaching files to your message. The files have to be JPEG, PNG, BMP, PDF-documents. Please be sure that you only add files up to 8 MB

Information on data protection can be found here.


 
Search

Refine Results

Gruppo Röchling

Divisioni

Lavora con noi

Assistenza

Stay informed
© 2024 Röchling
Contatto

Share

Print to PDF

Share this page:

Facebook
Twitter
Pinterest
Xing
LinkedIn
Recommend this page via Email

Newsletter Registration

Select Website

Roechling_Industrial_Banner.jpg
Materie plastiche per applicazioni tecniche

Industrial