Durostone® EPC 204
GFK-EP
sheet
Characteristics
- Low flammeability
- Epoxy (EP) resin matrix reinforced with an e-glass fabric
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 236735 | Durostone® EPC 204 pressed | sheet | sheet | 2.000 x 1.100 x 10 (+/-1) mm | 2,000 mm | 1,100 mm | 10 mm | |||
| No stock item (MOQ) | 236736 | Durostone® EPC 204 pressed | sheet | sheet | 2.000 x 1.100 x 12 (+/-1) mm | 2,000 mm | 1,100 mm | 12 mm | |||
| No stock item (MOQ) | 298575 | Durostone® EPC 204 pressed | sheet | sheet | 2.000 x 1.100 x 8 (+/-1) mm | 2,000 mm | 1,100 mm | 8 mm | |||
| No stock item (MOQ) | 362983 | Durostone® EPC 204 pressed | sheet | sheet | 2.000 x 1.100 x 5 (+/-1) mm | 2,000 mm | 1,100 mm | 5 mm |
Technical Specifications Durostone® EPC 204
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | ISO 1183 | g / cm3 | 2,0 |
| Flexural strength ┴ | ISO 178 | MPa | 500 |
| Flexural strength ┴ +150°C | ISO 178 | MPa | 350 |
| Modulus of elasticity in flexion ┴ | ISO 178 | MPa | 25000 |
| Modulus of elasticity in flexion ┴ +150°C | ISO 178 | MPa | 21000 |
| Compressive strength ┴ | ISO 604 | MPa | 500 |
| Tensile strength II | ISO 527 | MPa | 350 |
| Impact strength II (Charpy) | ISO 179 | kJ / m2 | 120 |
| Shear strength II | IEC 60893 | MPa | 35 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Flammability | UL 94 | / | V0 / 2mm |
| Temperature index | IEC 60216 | T.I. | 155 |
| Insulation class | IEC 60085 | / | F |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Water absorption (4mm thickness) | ISO 62 | % | < 0,1 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Electric strength 90°C under oil ┴ | IEC 60243 | kV / mm | 15 |
| Electric strength 90°C under oil II | IEC 60243 | kV/25mm | 100 |
| Insulation resistance | IEC 60167 | Ohm | 1012 |
| Comparative tracking index | IEC 60112 | CTI | 600 |
| Insulation resistance after 24 h water immersion | IEC 60167 | Ohm | 1010 |