LubX® CV+ blue
PE — PE-UHMW - PE 1000
LubX® CV is a sliding material especially for systems and machinery used in conveyor technology and automation. The material was developed for systems intended to be operated at higher velocities and pressure loads, meaning increased productivity. Scientific research shows: The material significantly improves system performance and efficiency. Even when used for high-load applications, it retains its excellent sliding characteristics and high wear resistance.
LubX® CV has:
- exceptionally good sliding properties
- at the same time exhibits a very low temperature development
- Both results in lower wear and a longer lifespan of the entire system.
bleu d'eau, similaire RAL 5021
plaque
Characteristics
- Good sliding properties even at higher load
- Good machinability
- GMP 2023/2006 EC compliant
Industries
Industrie agroalimentaire
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 508771 | LubX® CV+ blue extruded | Profil spécial | Profil spécial (R337) | bleu d'eau, similaire RAL 5021 | 50.000 x 24 x 18 mm | 50 000 mm | 24 mm | 18 mm | ||
| No stock item (MOQ) | 508882 | LubX® CV+ blue extruded | Profil spécial | Profil spécial (R540) | bleu d'eau, similaire RAL 5021 | 50.000 x 25 x 16 mm | 50 000 mm | 25 mm | 16 mm | ||
| No stock item (MOQ) | 505585 | LubX® CV+ blue pressed | plaque | plaque | bleu d'eau, similaire RAL 5021 | 10 x 1000 x 2000 mm | 2 000 mm | 1 000 mm | 10 mm |
Technical Specifications LubX® CV+ blue
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Densité | DIN EN ISO 1183-1 | g / cm3 | 0,94 |
| Water absorption | DIN EN ISO 62 | % | 0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
| Non-toxicity | + |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 19 |
| Elongation at break | DIN EN ISO 527 | % | >250 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 500 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | No break |
| Shore hardness | DIN EN ISO 868 | scale D | 60 |
| Sliding partner POM MOD A (0,75 m/s - 0,25 MPa) | REP – Tribology – Test | 0,12 | |
| Sliding partner POM MOD B (0,75 m/s - 0,25 MPa) | REP – Tribology – Test | 0,13 | |
| Sliding partner PA MOD (0,75 m/s - 0,25 MPa) | REP – Tribology – Test | 0,11 | |
| Sliding partner High steel grade (0,75 m/s - 0,25 MPa) | REP – Tribology – Test | 0,17 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 133 ... 135 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 (*) |
| Service temperature, long term | Average | °C | -150 ... 80 (*) |
| Service temperature, short term (max.) | Average | °C | 130 (*) |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1015 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | >1014 |