Play-Tec® UV-stabilized PCR bicolor
PE — PE-HD - PE 300
Aires de jeux : faites le plein de sécurité, de longévité et de couleur avec Play-Tec®
- Sécurité
- Longévité
- Qualité esthétique
bicolore vert/noir/vert
plaque
Characteristics
- Physiologically safe
- Good machinability
- UV-resistant
Industries
Sustainability
- Post-Consumer-Recycling material
- Recycling content up to 95%
- LCA available (ISO 14040/44)
Application Examples
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 480437 | Play-Tec® UV-stabilized PCR bicolor extruded | plaque | plaque | bicolore vert/noir/vert | 12 x 1220 x 2440 mm | 2 440 mm | 1 220 mm | 12 mm |
Technical Specifications Play-Tec® UV-stabilized PCR bicolor
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Densité | DIN EN ISO 1183-1 | g / cm3 | >0,96 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
| Flammability (Thickness 3 - 10 mm) | DIN 4102 | B2 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >25 |
| Elongation at yield stress | DIN EN ISO 527 | % | >8 |
| Elongation at break | DIN EN ISO 527 | % | >235 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1200 |
| Notched impact strength | DIN EN ISO 11542 | / | |
| Notched impact strength, RT | DIN EN ISO 179 EA1 | kJ / m2 | >4 |
| Notched impact strength, < 0°C | DIN EN ISO 179 EA1 | kJ / m2 | >3 |
| Shore hardness | DIN EN ISO 868 | scale D | >60 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Température de transistion vitreuse | ISO 11357-3 | °C | ∼ -60 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,90 |
| Service temperature, long term | Average | °C | -30 … 80 |
| Heat storage behavior lengthwise | ISO 14632 | % | 0,05 |
| Heat storage behavior crosswise | ISO 14632 | % | 0,04 |