Glastherm® HT 200

GFK-UP

Glastherm^® HT 200 is a heat insulation system with a high level of stability which is suitable for processes with a working temperature of up to 200 °C (392 °F). Glastherm^® HT 200 was developed specially for plastic and zinc die-casting moulds. It has good thermal insulation, enabling rapid die heating-up processes and therefore rapid start-up of the machines. Glastherm^® HT 200 is free of asbestos and can be easily cut and adapted with standard metal tools.

Maximum continuous operation temperature: 200 °C (392 °F)
High compressive strength: 230 MPa (at 200 °C)
Good thermal insulation

sheet

Characteristics

Fibre-reinforced composite material developed for applications in field of thermal insulation (max. continuous operating temperature 200°C)

Industries

Variants

	SKU	Name	Type	Type	Measurements	Length	Width	Thickness
No stock item (MOQ)	428269	Glastherm® HT 200 pressed	sheet	sheet	2.445 x 1.255 x 22 mm	2,445 mm	1,255 mm	22 mm
No stock item (MOQ)	443422	Glastherm® HT 200 pressed	sheet	sheet	2.445 x 1.255 x 27 mm	2,445 mm	1,255 mm	27 mm
No stock item (MOQ)	447666	Glastherm® HT 200 pressed	sheet	sheet	2.445 x 1.255 x 12 (+/-0,1) mm	2,445 mm	1,255 mm	12 mm

Technical Specifications Glastherm® HT 200

Mechanical properties

	Test Method	Unit	Guideline Value
Density	ISO 1183	g / cm³	1,9
Flexural strength ┴	ISO 178	MPa	200
Modulus of elasticity in flexion ┴	ISO 178	MPa	12000
Compressive strength ¹⁾┴	ISO 604	MPa	320
Compressive strength ¹⁾┴ +200°C	ISO 604	MPa	230
Tensile strength II	ISO 527	MPa	120
Impact strength ┴ (Charpy)	ISO 179	kJ / m²	100
Splitting force II	DIN 53463	N	2200

Thermal properties

	Test Method	Unit	Guideline Value
Thermal conductivity ²⁾┴		W / (m * K)	≈ 0,3
Coefficient of linear expansion II	TMA (Mettler)	10^-6 x K^-1	≈ 20
Max. continuous operating temperature		°C	200