Polystone® PPs (Homopolymer) white
PP-H
white, similar RAL 9010
sheetwelding rod
Characteristics
- High stiffness
- Very good welding and processing properties
- Chemical resistance
- Flame retardant
Industries
Semiconductor Front-End applications- Semiconductor Front-End Wet Bench
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 213540 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 10 mm | 3,000 mm | 1,500 mm | 10 mm | ||
| No stock item (MOQ) | 213541 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 2.440 (-1/+6) x 1.220 (-1/+3) x 10 (+/-0,4) mm | 2,440 mm | 1,220 mm | 10 mm | ||
| No stock item (MOQ) | 265857 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 4 mm | 3,000 mm | 1,500 mm | 4 mm | ||
| No stock item (MOQ) | 307975 | Polystone® PPs (Homopolymer) white extruded | welding rod | welding rod | white, similar RAL 9010 | Ø 3 (+/-0,2) mm | 3 mm | ||||
| No stock item (MOQ) | 309765 | Polystone® PPs (Homopolymer) white extruded | welding rod | welding rod | white, similar RAL 9010 | B=5 (+/-0,3) x 3,5 (-0,4/+0) mm | 5 mm | 3.5 mm | |||
| No stock item (MOQ) | 313215 | Polystone® PPs (Homopolymer) white extruded | welding rod | welding rod | white, similar RAL 9010 | Ø 4 (-0,3/+0,2) mm | 4 mm | ||||
| No stock item (MOQ) | 319050 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 5 mm | 3,000 mm | 1,500 mm | 5 mm | ||
| No stock item (MOQ) | 338335 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 6 mm | 3,000 mm | 1,500 mm | 6 mm | ||
| No stock item (MOQ) | 338336 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 8 mm | 3,000 mm | 1,500 mm | 8 mm | ||
| No stock item (MOQ) | 338337 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 12 mm | 3,000 mm | 1,500 mm | 12 mm | ||
| No stock item (MOQ) | 338338 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 20 mm | 3,000 mm | 1,500 mm | 20 mm | ||
| No stock item (MOQ) | 338340 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 15 mm | 3,000 mm | 1,500 mm | 15 mm | ||
| No stock item (MOQ) | 378250 | Polystone® PPs (Homopolymer) white extruded | welding rod | welding rod | white, similar RAL 9010 | Ø 4 (-0,3/+0,2) mm | 4 mm | ||||
| No stock item (MOQ) | 405916 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 10 mm | 3,000 mm | 1,500 mm | 10 mm | ||
| No stock item (MOQ) | 410022 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 5 mm | 3,000 mm | 1,500 mm | 5 mm | ||
| No stock item (MOQ) | 410023 | Polystone® PPs (Homopolymer) white extruded | sheet | sheet | white, similar RAL 9010 | 3.000 x 1.500 x 10 mm | 3,000 mm | 1,500 mm | 10 mm |
Technical Specifications Polystone® PPs (Homopolymer) white
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,93 |
| Water absorption | DIN EN ISO 62 | % | <0,1 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V2 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >30 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1300 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | >4 |
| Shore hardness | DIN EN ISO 868 | scale D | >67 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 162 ... 167 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,20 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 120 ... 190 |
| Service temperature, long term | Average | °C | 0 … 100 |
| Service temperature, short term (max.) | Average | °C | 150 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 81 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,4 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,00019 | |
| Volume resistivity | DIN EN 62631-3-1 | Ohm * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ohm | >1014 |
| Dielectric strength | IEC 60243 | kV / mm | >30 |