Sustamid® 6 MO black

PA — PA 6

MoS₂-reinforced polyamide - optimized for sliding and abrasion loads

Sustamid® 6G M anthracite is a shape-polymerized polyamide 6 modified with molybdenum disulphide (MoS₂). Compared to the unmodified grade Sustamid® 6G, it has a higher MoS₂ content, which leads to an increased degree of crystallization and a fine, homogeneous microstructure. This results in greater hardness and a slightly higher modulus of elasticity. The material also offers very good sliding and abrasion properties.

black
sheettubular barrod
QR-Code

Characteristics

  • High hardness
  • High rigidity
  • UV-resistant
  • High absorption of moisture of up to 3 % in standard atmosphere
  • High stiffness
  • High mechanical strength

Technical Specifications Sustamid® 6 MO black

Test MethodUnitGuideline Value
DensityDIN EN ISO 1183-1g / cm31,14
Water absorptionDIN EN ISO 62%3,0
Flammability (Thickness 3 mm / 6 mm)UL 94HB / HB

Test MethodUnitGuideline Value
Yield stressDIN EN ISO 527MPa80
Elongation at breakDIN EN ISO 527%50
Tensile modulus of elasticityDIN EN ISO 527MPa3200
Notched impact strengthDIN EN ISO 179kJ / m23
Shore hardnessDIN EN ISO 868scale D82

Test MethodUnitGuideline Value
Melting temperatureISO 11357-3°C220
Thermal conductivityDIN 52612-1W / (m * K)0,23
Thermal capacityDIN 52612kJ / (kg * K)1,70
Coefficient of linear thermal expansionDIN 5375210-6 / K90
Service temperature, long termAverage°C-40 … 85
Service temperature, short term (max.)Average°C160
Heat deflection temperatureDIN EN ISO 75, Verf. A, HDT°C75

Downloads

Contact

메시지에 파일을 첨부할 수 있습니다. 파일은 JPEG, PNG, BMP, PDF 문서여야 합니다. 파일 크기가 8MB 이하인지
확인하세요.

Information on data protection can be found here.

Renew
 
Search
Contact

Newsletter Registration

Select Website

Roechling_Industrial_Banner.jpg
기술 응용 분야를 위한 플라스틱

Industrial