Sustamid® 6 GF 30 black
PA — PA 6
The strong glass fibre type
Sustamid® 6 GF30 (PA 6 GF30) is a high-performance engineering material based on polyamide 6, reinforced with 30% glass fibers. The glass fiber reinforcement provides high mechanical strength, good dimensional stability, and improved heat resistance. The combination of stiffness, strength, and low creep makes it ideal for components subjected to continuous mechanical and thermal stress.
black
rod
Characteristics
- High heat deflection temperature
- Good noise absorption properties
- Vibration damping
- High abrasion resistance
- High stiffness
- Good compressive strength
- High mechanical strength
Industries
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 111184 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 20 x 3000 mm | 3,000 mm | 20 mm | |||
| No stock item (MOQ) | 111187 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 30 x 3000 mm | 3,000 mm | 30 mm | |||
| No stock item (MOQ) | 111189 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 40 x 3000 mm | 3,000 mm | 40 mm | |||
| No stock item (MOQ) | 111190 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 45 x 3000 mm | 3,000 mm | 45 mm | |||
| No stock item (MOQ) | 111191 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 50 x 3000 mm | 3,000 mm | 50 mm | |||
| No stock item (MOQ) | 111192 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 60 x 3000 mm | 3,000 mm | 60 mm | |||
| No stock item (MOQ) | 111193 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 70 x 3000 mm | 3,000 mm | 70 mm | |||
| No stock item (MOQ) | 111194 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 80 x 3000 mm | 3,000 mm | 80 mm | |||
| No stock item (MOQ) | 111196 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 100 x 3000 mm | 3,000 mm | 100 mm | |||
| No stock item (MOQ) | 111201 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 100 x 1000 mm | 1,000 mm | 100 mm | |||
| No stock item (MOQ) | 803495 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 80 x 1000 mm | 1,000 mm | 80 mm | |||
| No stock item (MOQ) | 803583 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 60 x 1000 mm | 1,000 mm | 60 mm | |||
| No stock item (MOQ) | 804055 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 30 x 1000 mm | 1,000 mm | 30 mm | |||
| No stock item (MOQ) | 804056 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 40 x 1000 mm | 1,000 mm | 40 mm | |||
| No stock item (MOQ) | 804058 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 50 x 1000 mm | 1,000 mm | 50 mm | |||
| No stock item (MOQ) | 804352 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 70 x 1000 mm | 1,000 mm | 70 mm | |||
| No stock item (MOQ) | 921613 | Sustamid® 6 GF 30 black extruded | rod | rod | black | Ø 20 x 1000 mm | 1,000 mm | 20 mm |
Technical Specifications Sustamid® 6 GF 30 black
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,35 |
| Water absorption | DIN EN ISO 62 | % | 2,0 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 85 |
| Elongation at break | DIN EN ISO 527 | % | 5 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 4500 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 4 |
| Shore hardness | DIN EN ISO 868 | scale D | 86 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 220 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,28 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,50 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 60 |
| Service temperature, long term | Average | °C | -30 … 110 |
| Service temperature, short term (max.) | Average | °C | 180 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 140 |