Sustamid® 6G LU red
PA — PA 6 G
coral red, similar RAL 3016
sheetrod
Characteristics
- Good sliding and wear behaviour
- Very low "stick-slip" effect
- High rigidity
- high absorption of moisture of up to 3 % in standard atmosphere
Variants
| SKU | Name | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|
| Not in stock (MOQ) | 102185 | Sustamid® 6G LU red in-mould polymerised | sheet | coral red, similar RAL 3016 | 10 x 1000 x 2000 mm | 2.000 mm | 1.000 mm | 10 mm | ||
| Not in stock (MOQ) | 643895 | Sustamid® 6G LU red in-mould polymerised | sheet | coral red, similar RAL 3016 | 27x 1000 x 2000 mm | 2.000 mm | 1.000 mm | 27 mm | ||
| Not in stock (MOQ) | 920525 | Sustamid® 6G LU red in-mould polymerised | rod | coral red, similar RAL 3016 | Ø 76 x 3050 mm | 3.050 mm | 76 mm | |||
| Not in stock (MOQ) | 920531 | Sustamid® 6G LU red in-mould polymerised | sheet | coral red, similar RAL 3016 | 27 x 1250 x 2500 mm | 2.500 mm | 1.250 mm | 27 mm |
Technical Specifications Sustamid® 6G LU red
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,14 |
| Water absorption | DIN EN ISO 62 | % | 2,0 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 70 |
| Elongation at break | DIN EN ISO 527 | % | 30 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3400 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 4 |
| Shore hardness | DIN EN ISO 868 | scale D | 82 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 214 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,25 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 80 |
| Service temperature, long term | Average | °C | -40 … 110 |
| Service temperature, short term (max.) | Average | °C | 160 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 90 |