Polystone® MK FL + AST black
PE — PE-UHMW - PE 1000
black, similar RAL 9005
profilerodsheet
Characteristics
- Certified according to EN 45545-2
- Self-extinguishing
- Antistatic
Variants
Technical Specifications Polystone® MK FL + AST black extruded
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >1,0 |
| Water absorption | DIN EN ISO 62 | % | 0,1 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V0 | |
| Molecular weight | - | 106 g/mol | ∼ 9 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >20 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1000 |
| Shore hardness | DIN EN ISO 868 | scale D | >63 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -200 … 80 |
| Service temperature, short term (max.) | Average | °C | 130 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 79 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 109 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 109 |
Technical Specifications Polystone® MK FL + AST black pressed
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >1,0 |
| Water absorption | DIN EN ISO 62 | % | 0,1 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V0 | |
| Molecular weight | - | 106 g/mol | ∼ 9 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >20 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1000 |
| Shore hardness | DIN EN ISO 868 | scale D | >63 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -200 … 80 |
| Service temperature, short term (max.) | Average | °C | 130 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 79 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 109 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 109 |