Sustamid® 6 MO black
PA — PA 6
MoS₂-reinforced polyamide - optimized for sliding and abrasion loads
Sustamid® 6G M anthracite is a shape-polymerized polyamide 6 modified with molybdenum disulphide (MoS₂). Compared to the unmodified grade Sustamid® 6G, it has a higher MoS₂ content, which leads to an increased degree of crystallization and a fine, homogeneous microstructure. This results in greater hardness and a slightly higher modulus of elasticity. The material also offers very good sliding and abrasion properties.
black
sheettubular barrod
Characteristics
- High hardness
- High rigidity
- UV-resistant
- High absorption of moisture of up to 3 % in standard atmosphere
- High stiffness
- High mechanical strength
Variants
Technical Specifications Sustamid® 6 MO black
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,14 |
| Water absorption | DIN EN ISO 62 | % | 3,0 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 80 |
| Elongation at break | DIN EN ISO 527 | % | 50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3200 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 3 |
| Shore hardness | DIN EN ISO 868 | scale D | 82 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 220 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,23 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 90 |
| Service temperature, long term | Average | °C | -40 … 85 |
| Service temperature, short term (max.) | Average | °C | 160 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 75 |