Polystone® M ESD 90 NC grey
PE — PE-UHMW - PE 1000
Polystone® M is an ultra-high molecular weight polyethylene (PE-UHMW/PE 1000) used to solve friction, wear and material flow problems in many industries. The material is characterized by excellent sliding properties, extreme wear resistance, high impact strength and very good resistance to chemicals and has established itself in technical applications. The material is available in various colors.
pantone grey 442 C
sheet
Characteristics
- Electrostatically dissipative
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 354976 | Polystone® M ESD 90 NC grey pressed | sheet | sheet | pantone grey 442 C | 12 x 1500 x 2500 (-50/+0) mm | 2,500 mm | 1,500 mm | 12 mm | ||
| No stock item (MOQ) | 354991 | Polystone® M ESD 90 NC grey pressed | sheet | sheet | pantone grey 442 C | 12 x 2500 x 6000 mm | 6,000 mm | 2,500 mm | 12 mm |
Technical Specifications Polystone® M ESD 90 NC grey
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,94 |
| Water absorption | DIN EN ISO 62 | % | 0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
| Molecular weight | - | 106 g/mol | ∼ 9 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | >20 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >700 |
| Notched impact strength | DIN EN ISO 11542 | kJ / m2 | >50 |
| Shore hardness | DIN EN ISO 868 | scale D | >63 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,90 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -150 … 80 |
| Service temperature, short term (max.) | Average | °C | 130 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 79 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Surface resistivity | DIN EN 62631-3-2 | Ω | 106 ... 109 |