Matrox® U 110 green
PE — PE-UHMW - PE 1000
Matrox® is outstanding for its extremely low coefficient of friction and high wear resistance and so optimally meets requirements for the lining of silos and bunkers.
Matrox® U 110 contains oxidation-retardant additives for a longer service life in the higher temperature range.
light green
sheet
Characteristics
- Low coefficient of friction
- Good wear properties
- High temperature resistance
- Corrosion resistant
- Low moisture absorption
- Good impact strength
Industries
Application Examples
Variants
Technical Specifications Matrox® U 110 green
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,93 |
| Water absorption | DIN EN ISO 62 | % | 0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
| Molecular weight | - | 106 g/mol | ∼ 9 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >650 |
| Notched impact strength | DIN EN ISO 11542-2 | kJ / m2 | >100 |
| Shore hardness | DIN EN ISO 868 | scale D | >63 |
| Wear resistance | Sand-slurry | 80 | |
| Sand Slurry | 1018 Steel=10 | ∼ 80 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,90 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -250 … 110 |
| Service temperature, short term (max.) | Average | °C | -250 ... 130 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 80 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 2,3 | |
| Dielectric dissipation factor (106 Hz) | IEC 60250 | 0,0001 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 1014 |
| Comparative tracking index | IEC 60112 | 600 | |
| Dielectric strength | IEC 60243 | kV / mm | >40 |