Durolight® S2
GFK-UP
Durolight® is a new developed insulating composite material especially designed to meet the thermal and mechanical requirements of load bearing supports. Durolight® is manufactured from a special formulation of selected synthetic resins in combination with high-strength glass reinforcements.
cream, similar RAL 9001
sheet
Characteristics
- Low thermal conductivity and high mechanical strength
- Glass-reinforced thermoset SMC high-pressure laminate developed for applications at cryogenic temperatures
Application Examples
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 343637 | Durolight® S2 pressed | sheet | sheet | 2.380 x 1.160 x 74,42 (-2,36/+3,35) mm | 2.380 mm | 1.160 mm | 74,42 mm | |||
| No stock item (MOQ) | 345686 | Durolight® S2 pressed | sheet | sheet | 2.380 x 1.160 x 49,8 (-1,91/+2,6) mm | 2.380 mm | 1.160 mm | 49,8 mm | |||
| No stock item (MOQ) | 360891 | Durolight® S2 pressed | sheet | sheet | 2.380 x 1.160 x 50,8 (+/-2) mm | 2.380 mm | 1.160 mm | 50,8 mm | |||
| No stock item (MOQ) | 361347 | Durolight® S2 pressed | sheet | sheet | 2.380 x 1.160 x 25,4 (+/-1,4) mm | 2.380 mm | 1.160 mm | 25,4 mm | |||
| No stock item (MOQ) | 383105 | Durolight® S2 pressed | sheet | sheet | 2.380 x 1.160 x 45 (-0/+3) mm | 2.380 mm | 1.160 mm | 45 mm | |||
| No stock item (MOQ) | 415949 | Durolight® S2 pressed | sheet | sheet | 2.460 x 1.140 x 24,16 (+/-1,4) mm | 2.460 mm | 1.140 mm | 24,16 mm | |||
| No stock item (MOQ) | 417951 | Durolight® S2 pressed | sheet | sheet | 1.730 x 1.160 x 25,4 (+/-1,4) mm | 1.730 mm | 1.160 mm | 25,4 mm | |||
| No stock item (MOQ) | 369314 | Durolight® S2 white pressed | sheet | sheet | cream, similar RAL 9001 | 2.380 x 1.160 x 60 (+/-0,2) mm | 2.380 mm | 1.160 mm | 60 mm |
Technical Specifications Durolight® S2
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | ISO 1183 | g / cm3 | 1,95 |
| Flexural strength 1)┴ 0°C | ISO 178 | MPa | 350 |
| Flexural strength 1)┴ +50°C | ISO 178 | MPa | 300 |
| Flexural strength 1)┴ +100°C | ISO 178 | MPa | 200 |
| Flexural strength 1)┴ +150°C | ISO 178 | MPa | 110 |
| Flexural strength 1)┴ -50°C | ISO 178 | MPa | 450 |
| Flexural strength 1)┴ -150°C | ISO 178 | MPa | 600 2) |
| Flexural strength 1)┴ -196°C | ISO 178 | MPa | 700 2) |
| Flexural strength 1)┴ -100°C | ISO 178 | MPa | 510 |
| Modulus of elasticity in flexion 1)┴ 0°C | ISO 178 | MPa | 18000 |
| Compressive strength ┴ 0°C | ISO 604 | MPa | 450 |
| Compressive strength ┴ +50°C | ISO 604 | MPa | 400 |
| Compressive strength ┴ +100°C | ISO 604 | MPa | 250 |
| Compressive strength ┴ +150°C | ISO 604 | MPa | 180 |
| Compressive strength ┴ -50°C | ISO 604 | MPa | 550 |
| Compressive strength ┴ -100°C | ISO 604 | MPa | 650 |
| Compressive strength ┴ -150°C | ISO 604 | MPa | 750 2) |
| Compressive strength ┴ -196°C | ISO 604 | MPa | 850 2) |
| Tensile strength II RT | ISO 527 | MPa | 180 |
| Impact strength ┴ (Charpy) RT | ISO 179 | kJ / m2 | 200 |
| Shear strength II RT | DIN EN 60893 | MPa | 25 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Thermal conductivity ┴ RT | W / (m * K) | ≈ 0,38 2)3) | |
| Thermal conductivity ┴ -50°C | W / (m * K) | ≈ 0,35 2)3) | |
| Thermal conductivity ┴ -196 | W / (m * K) | ≈ 0,27 2)3) |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Water absorption (method 1) | ISO 62 | % | < 0,2 |