Matrox® X grey
PE — PE-UHMW - PE 1000
Matrox® is outstanding for its extremely low coefficient of friction and high wear resistance and so optimally meets requirements for the lining of silos and bunkers.
Matrox® X is the premium product when it comes to wear resistance and hardness and is thus outstandingly suitable for extreme conditions of use.
light grey, similar RAL 7035
rodsheet
Characteristics
- Low coefficient of friction
- Good wear properties
- High hardness
Industries
Application Examples
Variants
Technical Specifications Matrox® X grey pressed
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | >0,98 |
| Water absorption | DIN EN ISO 62 | % | 0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
| Molecular weight | - | 106 g/mol | ∼ 9 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | >1000 |
| Notched impact strength | DIN EN ISO 11542 | kJ / m2 | >80 |
| Shore hardness | DIN EN ISO 868 | scale D | >65 |
| Wear resistance | Sand-slurry | 80 | |
| Sand Slurry | 1018 Steel=10 | ∼ 78 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 130 ... 135 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,40 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,90 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 ... 230 |
| Service temperature, long term | Average | °C | -250 … 80 |
| Service temperature, short term (max.) | Average | °C | 130 |
| Vicat softening temperature | DIN EN ISO 306, Vicat B | °C | 79 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1014 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | >1014 |