Our premium material EtroX® I CM UHT was specially developed to meet the high demands of the electronics, aerospace and semiconductor industries. As a special pure polyimide, it withstands particularly high temperatures and offers a low water absorption of 0,06%. EtroX® I CM UHT can be used on long term with 300°C to design components that offer significant advantages over other thermoplastics.
SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
---|---|---|---|---|---|---|---|---|---|---|---|
No stock item (MOQ) | 761034 | EtroX® I CM UHT natural pressed | sheet | sheet | natural | 16 x 395 x 395 mm | 395 mm | 395 mm | 16 mm | ||
No stock item (MOQ) | 772246 | EtroX® I CM UHT natural pressed | sheet | sheet | natural | 20 x 395 x 395 mm | 395 mm | 395 mm | 20 mm | ||
No stock item (MOQ) | 777991 | EtroX® I CM UHT natural pressed | sheet | sheet | natural | 25 x 395 x 395 mm | 395 mm | 395 mm | 25 mm |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Density | DIN EN ISO 1183-1 | g / cm3 | 1,43 |
Water absorption | DIN EN ISO 62 (23°C / 24h) | % | 0,06 |
Water absorption | DIN EN ISO 62 (23°C / 48h) | % | 0,1 |
Water absorption | DIN EN ISO 62 (23°C / 3 Weeks) | % | 0,4 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Elongation at break | DIN EN ISO 527 | % | 4 |
Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 4800 |
Tensile strength | DIN EN ISO 527 | MPa | 142 |
Impact strength | DIN EN ISO 179 | kJ / m2 | 40 |
Notched impact strength | DIN EN ISO 179 | kJ / m2 | 3 |
Shore hardness | DIN EN ISO 868 | scale D | 90 |
Elastic modulus of compression | DIN EN ISO 604 | MPa | 4000 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Glass transition temperature | ISO 11357-3 | °C | 270 |
Service temperature, short term (max.) | Average | °C | 450 |
Temp. of deflection under load, 1.80 MPa | ISO 75-1/-2 | °C | 265 |
Temp. of deflection under load, 0.45 MPa | ISO 75-1/-2 | °C | 304 |
Test Method | Unit | Guideline Value | |
---|---|---|---|
Volume resistivity | DIN EN 62631-3-1 | Ω * cm | >1011 |
Dielectric constant (1 MHz) | DIN EN IEC 62631-2-1 | 3,3 |