Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 809948 | Sustamid® 66 MO black calendered | 7 x 620 x 3000 mm | 3 000 mm | 620 mm | 7 mm | |||||
| No stock item (MOQ) | 112143 | Sustamid® 66 MO black extruded | Ø 20 x 3000 mm | 3 000 mm | 20 mm | ||||||
| No stock item (MOQ) | 611358 | Sustamid® 66 MO black extruded | 20 x 620 x 3000 mm | 3 000 mm | 620 mm | 20 mm | |||||
| No stock item (MOQ) | 611361 | Sustamid® 66 MO black extruded | 20 x 620 x 1000 mm | 1 000 mm | 620 mm | 20 mm | |||||
| No stock item (MOQ) | 611364 | Sustamid® 66 MO black extruded | 80 x 620 x 1000 mm | 1 000 mm | 620 mm | 80 mm | |||||
| No stock item (MOQ) | 611370 | Sustamid® 66 MO black extruded | 80 x 620 x 3000 mm | 3 000 mm | 620 mm | 80 mm | |||||
| No stock item (MOQ) | 618209 | Sustamid® 66 MO black extruded | 80 x 620 x 2000 mm | 2 000 mm | 620 mm | 80 mm | |||||
| No stock item (MOQ) | 637478 | Sustamid® 66 MO black extruded | Ø 35 x 3000 mm | 3 000 mm | 35 mm | ||||||
| No stock item (MOQ) | 652560 | Sustamid® 66 MO black extruded | Ø 35 x 1000 mm | 1 000 mm | 35 mm | ||||||
| No stock item (MOQ) | 658629 | Sustamid® 66 MO black extruded | 12 x 620 x 3000 mm | 3 000 mm | 620 mm | 12 mm | |||||
| No stock item (MOQ) | 663902 | Sustamid® 66 MO black extruded | 12 x 620 x 1000 mm | 1 000 mm | 620 mm | 12 mm | |||||
| No stock item (MOQ) | 665467 | Sustamid® 66 MO black extruded | Ø 140 x 3000 mm | 3 000 mm | 140 mm | ||||||
| No stock item (MOQ) | 665469 | Sustamid® 66 MO black extruded | Ø 140 x 1000 mm | 1 000 mm | 140 mm | ||||||
| No stock item (MOQ) | 677554 | Sustamid® 66 MO black extruded | Ø 140 x 2000 mm | 2 000 mm | 140 mm | ||||||
| No stock item (MOQ) | 729597 | Sustamid® 66 MO black extruded | Ø 130 x 3000 mm | 3 000 mm | 130 mm | ||||||
| No stock item (MOQ) | 733392 | Sustamid® 66 MO black extruded | 30 x 620 x 1000 mm | 1 000 mm | 620 mm | 30 mm | |||||
| No stock item (MOQ) | 766581 | Sustamid® 66 MO black extruded | Ø 16 x 3000 mm | 3 000 mm | 16 mm | ||||||
| No stock item (MOQ) | 928675 | Sustamid® 66 MO black extruded | 30 x 620 x 3000 mm | 3 000 mm | 620 mm | 30 mm | |||||
| No stock item (MOQ) | 931848 | Sustamid® 66 MO black extruded | Ø 75 x 3000 mm | 3 000 mm | 75 mm |
Technical Specifications Sustamid® 66 MO black calendered
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,15 |
| Water absorption | DIN EN ISO 62 | % | 2,8 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / V2 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 90 |
| Elongation at break | DIN EN ISO 527 | % | 20 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3400 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 2 |
| Shore hardness | DIN EN ISO 868 | scale D | 83 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 260 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,23 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 80 |
| Service temperature, long term | Average | °C | -30 … 95 |
| Service temperature, short term (max.) | Average | °C | 170 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 100 |
Technical Specifications Sustamid® 66 MO black extruded
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,15 |
| Water absorption | DIN EN ISO 62 | % | 2,8 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / V2 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 90 |
| Elongation at break | DIN EN ISO 527 | % | 20 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3400 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 2 |
| Shore hardness | DIN EN ISO 868 | scale D | 83 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 260 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,23 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 80 |
| Service temperature, long term | Average | °C | -30 … 95 |
| Service temperature, short term (max.) | Average | °C | 170 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 100 |