Sustamid® 6G LL natural
PA — PA 6 G
PA 6G with optimized combination of hardness and impact strength
Sustamid® 6 GLL is a shape-polymerized polyamide 6 modified with an impact-resistant monomer. The material offers increased toughness and is particularly suitable for components that are exposed to shock and impact loads.
natural
blocrodtubular bar
Characteristics
- Good sliding properties
- Good wear properties
- Good machinability
- Good impact strength
Variants
Technical Specifications Sustamid® 6G LL natural
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,13 |
| Water absorption | DIN EN ISO 62 | % | 2,3 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB / V2 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 64 |
| Elongation at break | DIN EN ISO 527 | % | 50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 2700 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 5 |
| Shore hardness | DIN EN ISO 868 | scale D | 80 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 209 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,27 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,70 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 80 |
| Service temperature, long term | Average | °C | -40 … 110 |
| Service temperature, short term (max.) | Average | °C | 170 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 95 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 3,7 | |
| Dielectric dissipation factor (50 Hz) | IEC 60250 | 0,02 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 1015 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 1013 |
| Comparative tracking index | IEC 60112 | 600 | |
| Dielectric strength | IEC 60243 | kV / mm | 20 |