Application Examples
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 373451 | LubX® AST black extruded | (R593) | 30.000 x 11,5 x 12 mm | 30 000 mm | 11,5 mm | 12 mm | ||||
| No stock item (MOQ) | 418756 | LubX® AST black extruded | (R699) | 6020 (-0/+30) x 18,4 x 6 mm | 6 020 mm | 18,4 mm | 6 mm | ||||
| No stock item (MOQ) | 460446 | LubX® AST black extruded | (R779) | 3000 (-0/+30) x 17 x 6,2 mm | 3 000 mm | 17 mm | 6,2 mm | ||||
| No stock item (MOQ) | 464768 | LubX® AST black extruded | (R789) | 3020 (-0/+30) x 7,95 x 5 mm | 3 020 mm | 7,95 mm | 5 mm | ||||
| No stock item (MOQ) | 471221 | LubX® AST black extruded | (R779) | 6000 (-0/+20) x 17 x 6,2 mm | 6 000 mm | 17 mm | 6,2 mm | ||||
| No stock item (MOQ) | 380271 | LubX® AST black pressed | 2.000 x 1.000 x 15 mm | 2 000 mm | 1 000 mm | 15 mm | |||||
| No stock item (MOQ) | 401972 | LubX® AST black pressed | 2.000 x 1.000 x 50 mm | 2 000 mm | 1 000 mm | 50 mm | |||||
| No stock item (MOQ) | 443420 | LubX® AST black pressed | 2.000 x 1.000 x 20 mm | 2 000 mm | 1 000 mm | 20 mm | |||||
| No stock item (MOQ) | 443440 | LubX® AST black pressed | 6000 x 2000 x 20 mm | 6 000 mm | 2 000 mm | 20 mm | |||||
| No stock item (MOQ) | 443548 | LubX® AST black pressed | 2000 x 1000 x 20 mm | 2 000 mm | 1 000 mm | 20 mm | |||||
| No stock item (MOQ) | 450813 | LubX® AST black pressed | 6.000 x 2.000 x 25 mm | 6 000 mm | 2 000 mm | 25 mm | |||||
| No stock item (MOQ) | 463802 | LubX® AST black pressed | 6000 x 2000 x 15 mm | 6 000 mm | 2 000 mm | 15 mm |
Technical Specifications LubX® AST black extruded
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 0,94 |
| Water absorption | DIN EN ISO 62 | % | <0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 20 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 650 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | no break |
| Shore hardness | DIN EN ISO 868 | scale D | 60 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 133 – 135 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 - 230 (*) |
| Service temperature, long term | Average | °C | -150 … 80 (*) |
| Service temperature, short term (max.) | Average | °C | 130 (*) |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Surface resistivity | DIN EN 62631-3-2 | Ohm | < 109 |
Technical Specifications LubX® AST black pressed
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 0,94 |
| Water absorption | DIN EN ISO 62 | % | <0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 20 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 650 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | no break |
| Shore hardness | DIN EN ISO 868 | scale D | 60 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 133 – 135 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 - 230 (*) |
| Service temperature, long term | Average | °C | -150 … 80 (*) |
| Service temperature, short term (max.) | Average | °C | 130 (*) |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Surface resistivity | DIN EN 62631-3-2 | Ohm | < 109 |