LubX® C white
PE — PE-UHMW - PE 1000
With LubX® C we offer a high performance material especially aligned to POM and steel, which has outstanding dry-running properties at its disposal. They have been especially developed for applications in materials-handling and automation technologies.
- Compared with conventional sliding materials, conveying systems equipped with LubX® C need considerably less energy.
- The considerably lower coefficient of friction of LubX® C eliminates the possibility of the slip-stick effect (backsliding) almost completely and thus increases process stability.
white, similar RAL 9010
profile
Characteristics
- Energy-saving
- Especially aligned to POM and Steel
- Noise-reducing
- Coefficient of friction with POM as sliding partner up to 75% less than of PE-UHMW
- Coefficient of friction with steel as sliding partner up to 60% less than of PE-UHMW
- Food compliant according to 10/2011/EU, 1935/2004/EC, FDA
Application Examples
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 468563 | LubX® C white extruded | Clamp profile | Clamp profile (R795) | white, similar RAL 9010 | 3000 (-0/+50) x 15,6 x 15,4 mm | 3 000 mm | 15,6 mm | 15,4 mm | ||
| No stock item (MOQ) | 468565 | LubX® C white extruded | Clamp profile | Clamp profile (R795) | white, similar RAL 9010 | 4000 (-0/+50) x 15,6 x 15,4 mm | 4 000 mm | 15,6 mm | 15,4 mm |
Technical Specifications LubX® C white
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 0,93 |
| Water absorption | DIN EN ISO 62 | % | <0,01 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | HB | |
| Non-toxicity | + | ||
| Moulding Compound PE | DIN ISO 1872-1 | UHMW-PE-QCD 35-3-4 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Sliding properties: partner POM (0,25 m/s - 0,25 MPa) | REP - Tribology - Test | 0,08 | |
| Sliding properties: partner POM (0,25 m/s - 0,25MPa) | REP - Tribology - Test | 0,11 | |
| Yield stress | DIN EN ISO 527 | MPa | 19 |
| Elongation at break | DIN EN ISO 527 | % | >50 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 500 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | no break |
| Shore hardness | DIN EN ISO 868 | scale D | 60 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | 133 – 135 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 150 - 230 (*) |
| Service temperature, long term | Average | °C | -150 … 80 (*) |
| Service temperature, short term (max.) | Average | °C | 130 (*) |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Volume resistivity | DIN EN 62631-3-1 | Ohm * cm | >1015 |
| Surface resistivity | DIN EN 62631-3-2 | Ohm | >1014 |