SustaPEI blue
PEI
The Unique Amorphous High Performance Polymer
With its natural amber-coloured transparency, SustaPEI is characterised by an extremely high level of strength across a wide temperature range. At 190°C, PEI, also known by its raw material name Ultem, exhibits a tensile stress of 50 MPa. This is roughly equivalent to the level of polycarbonate at room temperature. Its flame resistance (UL94 V0), low smoke density and toxicity, and high electrical insulation capacity are also unique. Typical applications can be found in the aerospace, electrical and semiconductor industries.
brilliant blue, similar RAL 5007
rod
Characteristics
- High stiffness even at high temperatures
- Low smoke development
- Good resistance against high energy radiation
Application Examples
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 806372 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 65 x 3000 mm | 3 000 mm | 65 mm | |||
| No stock item (MOQ) | 806373 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 65 x 1000 mm | 1 000 mm | 65 mm | |||
| No stock item (MOQ) | 806708 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 55 x 3000 mm | 3 000 mm | 55 mm | |||
| No stock item (MOQ) | 806864 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 85 x 1000 mm | 1 000 mm | 85 mm | |||
| No stock item (MOQ) | 807267 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 40 x 1000 mm | 1 000 mm | 40 mm | |||
| No stock item (MOQ) | 807268 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 40 x 3000 mm | 3 000 mm | 40 mm | |||
| No stock item (MOQ) | 920148 | SustaPEI blue extruded | rod | rod | brilliant blue, similar RAL 5007 | Ø 85 x 3000 mm | 3 000 mm | 85 mm |
Technical Specifications SustaPEI blue
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Density | DIN EN ISO 1183-1 | g / cm3 | 1,27 |
| Water absorption | DIN EN ISO 62 | % | 0,5 |
| Flammability (Thickness 3 mm / 6 mm) | UL 94 | V0 / V0 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Yield stress | DIN EN ISO 527 | MPa | 110 |
| Elongation at break | DIN EN ISO 527 | % | 12 |
| Tensile modulus of elasticity | DIN EN ISO 527 | MPa | 3100 |
| Notched impact strength | DIN EN ISO 179 | kJ / m2 | 4 |
| Shore hardness | DIN EN ISO 868 | scale D | 86 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Melting temperature | ISO 11357-3 | °C | - |
| Glass transition temperature | ISO 11357-3 | °C | 217 |
| Thermal conductivity | DIN 52612-1 | W / (m * K) | 0,24 |
| Thermal capacity | DIN 52612 | kJ / (kg * K) | 1,10 |
| Coefficient of linear thermal expansion | DIN 53752 | 10-6 / K | 45 |
| Service temperature, long term | Average | °C | -50 … 170 |
| Service temperature, short term (max.) | Average | °C | 210 |
| Heat deflection temperature | DIN EN ISO 75, Verf. A, HDT | °C | 200 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Dielectric constant | IEC 60250 | 3,2 | |
| Dielectric dissipation factor (50 Hz) | IEC 60250 | 0,0015 | |
| Volume resistivity | DIN EN 62631-3-1 | Ω * cm | 1015 |
| Surface resistivity | DIN EN 62631-3-2 | Ω | 1015 |
| Comparative tracking index | IEC 60112 | 150 | |
| Dielectric strength | IEC 60243 | kV / mm | 30 |