Glastherm® HT 200
Other
Glastherm® HT 200 is a heat insulation system with a high level of stability which is suitable for processes with a working temperature of up to 200 °C (392 °F). Glastherm® HT 200 was developed specially for plastic and zinc die-casting moulds. It has good thermal insulation, enabling rapid die heating-up processes and therefore rapid start-up of the machines. Glastherm® HT 200 is free of asbestos and can be easily cut and adapted with standard metal tools.
- Maximum continuous operation temperature: 200 °C (392 °F)
- High compressive strength: 230 MPa (at 200 °C)
- Good thermal insulation
sheetmachined part
Characteristics
- Fibre-reinforced composite material developed for applications in field of thermal insulation (max. continuous operating temperature 200°C)
Variants
| SKU | Name | Type | Type | Color | Measurements | Length | Width | Thickness | Height | ||
|---|---|---|---|---|---|---|---|---|---|---|---|
| No stock item (MOQ) | 428269 | Glastherm® HT 200 pressed | sheet | sheet | 22 x 1255 x 2445 mm | 2 445 mm | 1 255 mm | 22 mm | |||
| No stock item (MOQ) | 443422 | Glastherm® HT 200 pressed | sheet | sheet | 27 x 1255 x 2445 mm | 2 445 mm | 1 255 mm | 27 mm | |||
| No stock item (MOQ) | 447666 | Glastherm® HT 200 pressed | sheet | sheet | 12 (+/-0,1) x 1255 x 2445 mm | 2 445 mm | 1 255 mm | 12 mm | |||
| No stock item (MOQ) | 505348 | Glastherm® HT 200 pressed | machined part | machined part | 2.046 x 327,5 x 20 (+/-0,1) mm | 2 046 mm | 327,5 mm | 20 mm | |||
| No stock item (MOQ) | 505352 | Glastherm® HT 200 pressed | machined part | machined part | 1.532,5 x 216 x 20 (+/-0,1) mm | 1 532,5 mm | 216 mm | 20 mm | |||
| No stock item (MOQ) | 505354 | Glastherm® HT 200 pressed | machined part | machined part | 1.035 x 216 x 20 (+/-0,1) mm | 1 035 mm | 216 mm | 20 mm |
Technical Specifications Glastherm® HT 200
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Hustota | ISO 1183 | g / cm3 | 1,9 |
| Pevnost v ohybu ┴ | ISO 178 | MPa | 200 |
| Modul pružnosti v ohybu ┴ | ISO 178 | MPa | 12000 |
| Pevnost v tlaku 1)┴ | ISO 604 | MPa | 320 |
| Pevnost v tlaku 1)┴ +200 °C | ISO 604 | MPa | 230 |
| Pevnost v tahu II | ISO 527 | MPa | 120 |
| Rázová houževnatost ┴ (Charpy) | ISO 179 | kJ / m2 | 100 |
| Štěpná síla II | DIN 53463 | N | 2200 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Tepelná vodivost 2)┴ | W / (m * K) | ≈ 0,3 | |
| Součinitel lineární roztažnosti II | TMA (Mettler) | 10-6 x K-1 | ≈ 20 |
| Maximální trvalá provozní teplota | °C | 200 |
| Test Method | Unit | Guideline Value | |
|---|---|---|---|
| Absorpce vody (metoda 1) | ISO 62 | % | 0,1 |